Cordierite Mullite Plate, Mullite Plate, Cordierite Plate manufacturer / supplier in China, offering Good Thermal Shock Cordierite Mullite Ceramic Thermal Plate, Al2O3 Coffee/ Pepper Ceramic Grinder, 99.5% Al2O3 Ceramic Furnace Tube and so on.

Supplier Homepage Product List Refactory Ceramics Mullite Ceramics Good Thermal Shock Cordierite Mullite Ceramic Thermal Plate

Good Thermal Shock Cordierite Mullite Ceramic Thermal Plate

FOB Price: Get Latest Price
Min. Order: 20 Pieces
Production Capacity: 1000000PCS/Month
Transport Package: Wooden Box or Carton
Payment Terms: L/C, T/T, Paypal, Money Gram, Western Union

Request a custom order and have something just for you!

Send Customized Request

Basic Info.

Model NO.:HB74
Refractoriness (℃):1580< Refractoriness< 1770
Feature:Long Time Materials, Instant Materials
Type:Heat-Resistant Material
Shape:Plate
Material:Mullite
Temperature of Application:1350c
Acid-Proof Alkaline:Good
Refractoriness:1600c
Flexural Strength(20°c):12MPa
Trademark:Highborn
Specification:ROHS
Origin:Jiangsu/China
HS Code:6906000000

Product Description


Cordierite Insulator& Cordierite Ceramic& Cordierite
 
Product Description
  
Cordierite is a ceramic used in heat shock applications that would crack and shatter most other ceramic materials.
Kiln furniture is made of cordierite because it will survive thousands of heating and cooling cycles.
At Paratech all of our production is placed in cordierite trays known as saggers to be used in the kiln during the firing cycle.
Small cordierite parts can be dry powder pressed. Large cordierite pieces are formed by slip casting.
Slip casting is a process where the ceramic material is mixed with water and poured into a plaster mold. After a few hours the plaster draws off the water from the mix and the sagger or other shape can be released from the mold. Parts are then dried and fired.
Cordierite ceramic
 

Item

Unit

Index

 
Material

Al2O3

%

>38.2

SiO2

%

<51.5

MgO

%

>6.7

Fe2O3

%

<0.9

Density

g/cm3

1.99

Open porosity

Mpa

21.63

Flexural strength(20°C)

Mpa

12

Thermal shock stability 1100°C(cold water)times

Times

20

Refractoriness

°C

1600

Temperature

°C

1350

Send your message to this supplier
Avatar
Mrs. Emily Miao
*From
To Mrs. Emily Miao
*Message
Enter between 20 to 4,000 characters.
This is not what you are looking for? Post a Sourcing Request Now

Lianyungang Highborn Technology Co., Ltd.

- Jiangsu, China
- Manufacturer/Factory, Trading Company

Gold Member Since 2015
Audited Supplier
  • Sample Available
  • OEM/ODM Service